GB Cr5Mo1V | JIS SKD12 | DIN 1.2363 | BS BA2 | ASTM A2/T30102 Cold Work Tool Steel
Quick Details
1: AISI A2 steel introduction
AISI A2 tool steel is one of 'A' group cold works steel in ASTM A681 standard. A2 Tool Steel is a versatile, air hardening chromium alloy tool steel that replaces O1 tool steel when safer hardening, less distortion and increased wear resistance are required. AISI type A2 steel is intermediate in wear resistance between O1 oil-hardening tool steel and D2 high-carbon, high-chromium tool steel.
2: AISI A2 Steel equivalent
| Country | China | Japan | Germany | USA | UK |
| Standard | GB/T 1299 | JIS G4404 | DIN EN ISO4957 | ASTM A681 | BS 4659 |
| Grade | Cr5Mo1V | SKD12 | 1.2363/X100CrMoV5 | A2/T30102 | BA2 |
| Grade | C | Mn | P | S | Si | Cr | V | Mo | ||||||
| A2/T30102 | 0.95 | 1.05 | 0.40 | 1.00 | 0.03 | 0.03 | 0.10 | 0.50 | 4.75 | 5.50 | 0.15 | 0.50 | 0.90 | 1.40 |
| 1.2363/ X100CrMoV5 |
0.95 | 1.05 | 0.40 | 0.80 | 0.03 | 0.03 | 0.10 | 0.40 | 4.80 | 5.50 | 0.15 | 0.35 | 0.90 | 1.20 |
| SKD12 | 0.95 | 1.05 | 0.40 | 0.80 | 0.03 | 0.03 | 0.10 | 0.40 | 4.80 | 5.50 | 0.15 | 0.35 | 0.90 | 1.20 |
| BA2 | 0.95 | 1.05 | 0.30 | 0.70 | 0.035 | 0.035 | . . . | 0.40 | 4.75 | 5.25 | 0.15 | 0.40 | 0.90 | 1.10 |
The mechanical properties mainly include tensile strength, yield strength, elongation, area or reduction, hardness, impact value, non-metalic inclusion etc. Different heat treatment, the mechanical properties will be different, such as normalized, tempered, QT. If you want to know the properties, kindly contact the salesman.
5: AISI A2 steel overviews
| Size | Round | Dia 6-1200mm |
| Plate/Flat/Block | Thickness 6mm-500mm |
|
| Width 20mm-1000mm |
||
| Process | EAF+LF+VD+Forged+Heat treatment(optional) | |
| Heat treatment | Normalized ; Annealed ; Quenched ; Tempered | |
| Surface condition | Black; Peeled; Polished; Machined; Grinded; Turned; Milled | |
| Delivery condition | Forged; Hot rolled; Cold drawn | |
| Test | Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc. | |
| Payment terms | T/T;L/C;/Money gram/ Paypal | |
| Trade terms | FOB; CIF; C&F; etc.. | |
| Packing | Standard Packages, or as Customers Request | |
| Delivery time | 30-45 days | |
| Application | AISI A2 is suitable for applications such as Blanking dies, block and ring gauges, coining, cold forming, cold trimming and forming dies, cold shears, rolls, knurls and knurling tools, machine parts, mandrels, punches and punch plates, reamers, shear and slitter blades, stamping dies and threading tapes. | |
6: Heat Treatment
Stress relieving
After heavy grinding or machine it is advisable to stress relieve tool steel A2 to reduce the danger of cracking or distortion during subsequent heat treatments. Heat slowly to 670-700°C, soak for a minimum of two hours per 25mm of section then cool down in the furnace.
Annealing
To prevent decarburization use a controlled atmosphere furnace or pack in a sealed container using some inert material. To anneal A2 tool steel for lowest hardness, heat slowly to 899°C(1650°F) and hold at this temperature for about two hours per inch of greatest cross-section. Cool steel A2 at a rate of 20°F (10°C) per hour to 650°C (1200°F) and reheat to 732°C (1350°F); hold 3 hours per inch of greatest cross-section; furnace cool at 20 degrees per hour to 593°C (1100°F); then furnace-cool to 482°C (900°F) and air-cool.
Hardening
Preheating temperature: 1200-1380°F (650-750°C). Austenitizing temperature: 1700 -1780°F (925-970°C) but usually 1720-1760°F (940-960°C).
Tempering
Choose the tempering temperature according to the hardness required by reference to the tempering graph.
Heat uniformly and thoroughly to the desired temperature and hold for 25 minutes per cm of thickness. Tool steel A2 can be double tempering, after intermediate cooling to room temperature. Temper at 200°C for a balance of hardness and strength or 350°C where strength is more important than hardness. A minimum holding time of 2 hours per inch of greatest cross-section should be used.
Quenching
Martempering bath or fluidized bed at 360-430°F (180-220°C) or 840-1020°F (450-550°C) then cool in air
Circulating air or atmosphere
Vacuum furnace with overpressure of gas at cooling
Oil (only for small and uncomplicated tools)
7: Delivery condition
For hot rolled plate, usually the delivery condition is hot rolled, annealed, black surface.
| GB GB/T 1299 |
JIS JIS G4404 |
DIN (W-Nr.) DIN EN ISO4957 |
AISI/ASTM ASTM A681 |
BS BS 4659 |
| Cold Work Tool Steel | ||||
| Cr12 | SKD1 | 1.2080/X210Cr12 | D3 | |
| Cr5Mo1V | SKD12 | 1.2363/X100CrMoV5 | A2/T30102 | BA2 |
| Cr12MoV | 1.2601 | D5 | ||
| Cr12Mo1V1 | SKD11 | 1.2379/X153CrMo12 | D2 | |
| X210CrW12 | SKD2 | 1.2436 | D6 | |
| 9CrWMn | SKS3 | 1.2510/100MnCrW4 | O1 | |
| 9Mn2V | 1.2842 / 90MnCrV8 | O2 | B02 | |
| 5CrNiMo | SKT4 | 1.2713 | L6/T61206 | BH224/5 |
| Hot work Tool Steel | ||||
| 1.2355/50CrMoV13-15 | S7/T41907 | |||
| 5CrNiMoV | 1.2714 | 6F3 | ||
| 5CrNi4Mo | 1.2767 | 6F7 | ||
| SKD7 | 1.2365/32CrMoV12-28 | H10/T20810 | BH10 | |
| 4Cr5MoV | SKD6 | 1.2343/X37CrMoV5-1 | H11/T20811 | BH11 |
| 4Cr5MoSiV1 | SKD61 | 1.2344/X40CrMoV5-1 | H13 | |
| SKD62 | 1.2605/X35CrWMoV5 | H12/T20812 | BH12 | |
| 3Cr2W8V | SKD5 | 1.2581 | H21 | |
| Plastic Mould Steel | ||||
| 3Cr2Mo | 1.2311 | P20 | ||
| NAK80 | 1.2312 | P20+S / P21 | ||
| 3Cr2MnNiMo | 1.2738 | P20+Ni / 718 | ||
| 4Cr13 | SUS420J2 | 1.2083 | 415 | |
| 3Cr17+S | SUS420F | 1.2085 | ||
| 3Cr17Mo | SUS420J | 1.2316 | ||
| Engineering Steel | ||||
| GB GB/T 699 |
JIS JIS G4051 |
DIN (W-Nr.) EN 10083-2 |
AISI/ASTM ASTM A20 |
EN / BS |
| 1018 | EN2C | |||
| 20 | S20C | C20/1.1151 | 1020 | EN3B /070M20 |
| S35C | C35 | 1035 | ||
| 1040 | EN8/080M40 | |||
| 45 | S45C | C45/1.1191 | 1045 | EN8D/C45E |
| 50 | S50C | 1050 | ||
| S55C | 1055 | EN9/070M55 | ||
| Q345 | S355/ST52-3/1.1170 | EN14/150M19 | ||
| GB GB/T 3077 |
JIS JIS G4105/JIS G4103 |
DIN (W-Nr.) EN 10250 |
AISI/ASTM ASTM A29 |
BS BS 970 |
| 40Cr | SCr440 | 41Cr4(1.7035) | 5140 | |
| SCM420 | 18CrMo4/1.7243 | 4118 | ||
| 30CrMo | SCM430 | 25CrMo4/1.7218 | 4130 | 708A25/708M25 |
| 42CrMo | SCM440 | 42crmo4/1.7225 | 4140 | EN19/709M40 |
| 4145 | ||||
| 4330 | ||||
| 40CrNiMoA | SNCM 439/SNCM8 | 36CrNiMo4/1.6511 | 4340 | EN24/817M40 |
| 40NiMoCr10-5/1.6745 | EN26 | |||
| 34CrNiMo6 / 1.6582 | 4337 | |||
| 30CrNiMo16-6/1.6747 | EN30B/835M30 | |||
| 32CrMo12/1.7361 | EN40B/722M24 | |||
| SCM415 | 16MnCr5 / 1.7131 | 5115 | ||
| 15CrNi6/1.5919 | 3115 | |||
| 16NiCr4/1.5714 | EN351/635M15 | |||
| 4615/4617 | EN34/665M17 | |||
| 14NiCr4/1.5752 | 3310/3415 | EN36/655M13 | ||
| 15NiCrMo16-5/1.6723 | EN39/835M15 | |||
| 18CrNiMo7-6 (1.6587) | 4815 | |||
| SNCM220 | 1.6523/21NiCrMo2 | 8620 | 805M20 | |
| 20CrNiMo5 | EN353 | |||
| GCr15 | 52100/1.3505 | EN31/535A99 | ||
| Stainless Steel | ||||
| SUS440C | X105CrMo17/1.4125 | S44004/440C | ||
| Wear-resisting Steel | ||||
| GB | JIS | DIN (W-Nr.) | AISI/ASTM | SSAB |
| NM400 | HB400 | |||
| NM500 | HB500 | |||
| Spring Steel | ||||
| GB | JIS | DIN (W-Nr.) | AISI/ASTM | SSAB |
| 65MN | 1066 | |||
| 60Si2Mn | SUP6 | 60Si7 | 9260 | |
| 60Si2MnA | SUP7 | 60Si7 | 9260 | |
| 55CrMnA | SUP9 | 55Cr3 | 5155 | |
| 60CrMnA | SUP9A | 5160 | ||
| 50CrVA | SUP10 | 51CrV4 | 6150 | |
| High Speed Steel | ||||
| GB | JIS JIS G4403 |
DIN (W-Nr.) DIN EN ISO 4957 |
AISI/ASTM ASTM A600 |
BS BS 4659 |
| SKH51 | 1.3343 | M2 | ||
| SKH55 | 1.3243/HS6-5-2-5 | M35 | ||
| SKH59 | 1.3247/HS2-9-1-8 | M42 | ||
| SKH2 | HS18-0-1/1.3355 | T1 | ||
| SKH3 | S 18-1-2-5/1.3255 | T4/T12004 | ||
| SKH4 | 1.3265/S18-1-2-10 | T5/T12005 | BT5 | |
| All kinds of forging parts according to Drawing | ||||
| Size | Round | Dia 8-1200mm |
| Plate/Flat/Block | Thickness 10mm-800mm |
|
| Width 20mm-2000mm |
||
| Heat treatment | Normalized ; Annealed ; Quenched ; Tempered | |
| Surface condition | Black; Peeled; Polished; Machined; Grinded; Turned; Milled | |
| Delivery condition | Forged; Hot rolled; Cold drawn | |
| Test | Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc. | |
| Payment terms | T/T;L/C;/Money gram/ Paypal | |
| Trade terms | FOB; CIF; C&F; etc.. | |
| Delivery time | 30-45 days | |
Hunan Qilu Industrial Co., Ltd has the capacity to forge round steel, steel flat, square steel, module, shaft and roller, etc. The main specifications of the products include Φ80-1000mm forging materials and 80-1200mm square billets and which the maximum piece weight can reach 50T.
The company owns advanced special steel smelting facilities and forging processing equipments, the main steel-making equipment include 2 sets of 50t ultra-high power electric arc furnaces,2 sets of 60t LF refining furnaces,1 set of 60t vacuum degassing refining furnace and 4 sets of 1-20t electroslag re-melting furnaces.