Audited Supplier JIS SKD62 | DIN 1.2605 | BS BH12 | ASTM H12 Hot Work Tool Steel
Quick Details
1: AISI H12 steel introduction
AISI H12 tool steel is a 4.75~5.5% chromium, general-purpose hot work steel. H12 tool steel contains (0.2~0.5%) less vanadium than the widely-used H13 hot works tool steel (0.8~1.2%). ASTM/AISI H12 Steel is a deep-hardening, air-hardening steel that exhibits minimal size change during heat treatmnet. H12 tool steel material has good resistance to thermal fatique cracking (heat cracking) and excellent resistnce to gross cracking and thermal shock when water cooled in service. So, we could say H-12 tool steel mainly has the following characteristics:
| Country | China | Japan | Germany | USA | UK |
| Standard | GB/T 1299 | JIS G4404 | DIN EN ISO4957 | ASTM A681 | BS 4659 |
| Grade | SKD62 | 1.2605/X35CrWMoV5 | H12/T20812 | BH12 |
| Grade | C | Mn | P | S | Si | Cr | V | W | Mo | Ni | Cu | Sn | |||||||
| H12/ T20812 |
0.30 | 0.4 | 0.2 | 0.6 | 0.03 | 0.03 | 0.80 | 1.25 | 4.75 | 5.50 | 0.2 | 0.5 | 1.00 | 1.70 | 1.25 | 1.75 | … | … | … |
| 1.2605 /X35Cr WMoV5 |
0.32 | 0.4 | 0.2 | 0.5 | 0.03 | 0.02 | 0.80 | 1.20 | 4.75 | 5.50 | 0.2 | 0.5 | 1.10 | 1.60 | 1.25 | 1.60 | … | … | … |
| SKD62 | 0.32 | 0.4 | 0.2 | 0.5 | 0.03 | 0.02 | 0.80 | 1.20 | 4.50 | 5.50 | 0.2 | 0.5 | 1.00 | 1.60 | 1.00 | 1.60 | … | … | … |
| BH12 | 0.30 | 0.4 | … | 0.4 | 0.35 | 0.35 | 0.85 | 1.15 | 4.75 | 5.25 | … | 0.5 | 1.25 | 1.75 | 1.25 | 1.75 | 0.4 | 0.2 | 0.05 |
The mechanical properties mainly include tensile strength, yield strength, elongation, area or reduction, hardness, impact value, non-metalic inclusion etc. Different heat treatment, the mechanical properties will be different, such as normalized, tempered, QT. If you want to know the properties, kindly contact the salesman.
5: AISI H12 steel overviews
| Size | Round | Dia 6-1200mm |
| Plate/Flat/Block | Thickness 6mm-500mm |
|
| Width 20mm-1000mm |
||
| Process | EAF+LF+VD+Forged+Heat treatment(optional) | |
| Heat treatment | Normalized ; Annealed ; Quenched ; Tempered | |
| Surface condition | Black; Peeled; Polished; Machined; Grinded; Turned; Milled | |
| Delivery condition | Forged; Hot rolled; Cold drawn | |
| Test | Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc. | |
| Payment terms | T/T;L/C;/Money gram/ Paypal | |
| Trade terms | FOB; CIF; C&F; etc.. | |
| Packing | Standard packages or as per customers request. | |
| Delivery time | 30-45 days | |
| Application | AISI H12 tool steel are suitable for Extrusion indushry: dies and inner liner for extrusion, extrusion tools Forging Industry: forming dies, press dies Die casting industry: dies for die-carbideTool Industry: hot punch, hot shear blades, immediate roller for cold rolling etc.. | |
6. Heat Treatment
Annealing
Heating Steel H-12 slowly and uniformly to 845~900ºC, furnace cooling to 540ºC at a rate 10~20ºC/hr. Hardness HB 229 max
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating H12 steel to approx.650oC, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Preheating (1): Heat H-12 steel to approx. 540~650ºC, holding 30 minutes per 25mm.
Preheating (2): Heat H12 tool steels to approx. 845~870ºC, holding 30 minutes per 25mm.
Austenitizing: Heat steel H12 to approx. 1010~1050ºC, holding 30 minutes per 25 mm.
Quenching: By oil or air.
Tempering
Tempering temperature: 520-700oC, hold at least 2 hours, air cooling and double tempering.
7: Delivery condition
For hot rolled plate, usually the delivery condition is hot rolled, annealed, black surface.
| GB GB/T 1299 |
JIS JIS G4404 |
DIN (W-Nr.) DIN EN ISO4957 |
AISI/ASTM ASTM A681 |
BS BS 4659 |
| Cold Work Tool Steel | ||||
| Cr12 | SKD1 | 1.2080/X210Cr12 | D3 | |
| Cr5Mo1V | SKD12 | 1.2363/X100CrMoV5 | A2/T30102 | BA2 |
| Cr12MoV | 1.2601 | D5 | ||
| Cr12Mo1V1 | SKD11 | 1.2379/X153CrMo12 | D2 | |
| X210CrW12 | SKD2 | 1.2436 | D6 | |
| 9CrWMn | SKS3 | 1.2510/100MnCrW4 | O1 | |
| 9Mn2V | 1.2842 / 90MnCrV8 | O2 | B02 | |
| 5CrNiMo | SKT4 | 1.2713 | L6/T61206 | BH224/5 |
| Hot work Tool Steel | ||||
| 1.2355/50CrMoV13-15 | S7/T41907 | |||
| 5CrNiMoV | 1.2714 | 6F3 | ||
| 5CrNi4Mo | 1.2767 | 6F7 | ||
| SKD7 | 1.2365/32CrMoV12-28 | H10/T20810 | BH10 | |
| 4Cr5MoV | SKD6 | 1.2343/X37CrMoV5-1 | H11/T20811 | BH11 |
| 4Cr5MoSiV1 | SKD61 | 1.2344/X40CrMoV5-1 | H13 | |
| SKD62 | 1.2605/X35CrWMoV5 | H12/T20812 | BH12 | |
| 3Cr2W8V | SKD5 | 1.2581 | H21 | |
| Plastic Mould Steel | ||||
| 3Cr2Mo | 1.2311 | P20 | ||
| NAK80 | 1.2312 | P20+S / P21 | ||
| 3Cr2MnNiMo | 1.2738 | P20+Ni / 718 | ||
| 4Cr13 | SUS420J2 | 1.2083 | 415 | |
| 3Cr17+S | SUS420F | 1.2085 | ||
| 3Cr17Mo | SUS420J | 1.2316 | ||
| Engineering Steel | ||||
| GB GB/T 699 |
JIS JIS G4051 |
DIN (W-Nr.) EN 10083-2 |
AISI/ASTM ASTM A20 |
EN / BS |
| 1018 | EN2C | |||
| 20 | S20C | C20/1.1151 | 1020 | EN3B /070M20 |
| S35C | C35 | 1035 | ||
| 1040 | EN8/080M40 | |||
| 45 | S45C | C45/1.1191 | 1045 | EN8D/C45E |
| 50 | S50C | 1050 | ||
| S55C | 1055 | EN9/070M55 | ||
| Q345 | S355/ST52-3/1.1170 | EN14/150M19 | ||
| GB GB/T 3077 |
JIS JIS G4105/JIS G4103 |
DIN (W-Nr.) EN 10250 |
AISI/ASTM ASTM A29 |
BS BS 970 |
| 40Cr | SCr440 | 41Cr4(1.7035) | 5140 | |
| SCM420 | 18CrMo4/1.7243 | 4118 | ||
| 30CrMo | SCM430 | 25CrMo4/1.7218 | 4130 | 708A25/708M25 |
| 42CrMo | SCM440 | 42crmo4/1.7225 | 4140 | EN19/709M40 |
| 4145 | ||||
| 4330 | ||||
| 40CrNiMoA | SNCM 439/SNCM8 | 36CrNiMo4/1.6511 | 4340 | EN24/817M40 |
| 40NiMoCr10-5/1.6745 | EN26 | |||
| 34CrNiMo6 / 1.6582 | 4337 | |||
| 30CrNiMo16-6/1.6747 | EN30B/835M30 | |||
| 32CrMo12/1.7361 | EN40B/722M24 | |||
| SCM415 | 16MnCr5 / 1.7131 | 5115 | ||
| 15CrNi6/1.5919 | 3115 | |||
| 16NiCr4/1.5714 | EN351/635M15 | |||
| 4615/4617 | EN34/665M17 | |||
| 14NiCr4/1.5752 | 3310/3415 | EN36/655M13 | ||
| 15NiCrMo16-5/1.6723 | EN39/835M15 | |||
| 18CrNiMo7-6 (1.6587) | 4815 | |||
| SNCM220 | 1.6523/21NiCrMo2 | 8620 | 805M20 | |
| 20CrNiMo5 | EN353 | |||
| GCr15 | 52100/1.3505 | EN31/535A99 | ||
| Stainless Steel | ||||
| SUS440C | X105CrMo17/1.4125 | S44004/440C | ||
| Wear-resisting Steel | ||||
| GB | JIS | DIN (W-Nr.) | AISI/ASTM | SSAB |
| NM400 | HB400 | |||
| NM500 | HB500 | |||
| Spring Steel | ||||
| GB | JIS | DIN (W-Nr.) | AISI/ASTM | SSAB |
| 65MN | 1066 | |||
| 60Si2Mn | SUP6 | 60Si7 | 9260 | |
| 60Si2MnA | SUP7 | 60Si7 | 9260 | |
| 55CrMnA | SUP9 | 55Cr3 | 5155 | |
| 60CrMnA | SUP9A | 5160 | ||
| 50CrVA | SUP10 | 51CrV4 | 6150 | |
| High Speed Steel | ||||
| GB | JIS JIS G4403 |
DIN (W-Nr.) DIN EN ISO 4957 |
AISI/ASTM ASTM A600 |
BS BS 4659 |
| SKH51 | 1.3343 | M2 | ||
| SKH55 | 1.3243/HS6-5-2-5 | M35 | ||
| SKH59 | 1.3247/HS2-9-1-8 | M42 | ||
| SKH2 | HS18-0-1/1.3355 | T1 | ||
| SKH3 | S 18-1-2-5/1.3255 | T4/T12004 | ||
| SKH4 | 1.3265/S18-1-2-10 | T5/T12005 | BT5 | |
| All kinds of forging parts according to Drawing | ||||
| Size | Round | Dia 8-1200mm |
| Plate/Flat/Block | Thickness 10mm-800mm |
|
| Width 20mm-2000mm |
||
| Heat treatment | Normalized ; Annealed ; Quenched ; Tempered | |
| Surface condition | Black; Peeled; Polished; Machined; Grinded; Turned; Milled | |
| Delivery condition | Forged; Hot rolled; Cold drawn | |
| Test | Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc. | |
| Payment terms | T/T;L/C;/Money gram/ Paypal | |
| Trade terms | FOB; CIF; C&F; etc.. | |
| Delivery time | 30-45 days | |
Hunan Qilu Industrial Co., Ltd has the capacity to forge round steel, steel flat, square steel, module, shaft and roller, etc. The main specifications of the products include Φ80-1000mm forging materials and 80-1200mm square billets and which the maximum piece weight can reach 50T.
The company owns advanced special steel smelting facilities and forging processing equipments, the main steel-making equipment include 2 sets of 50t ultra-high power electric arc furnaces,2 sets of 60t LF refining furnaces,1 set of 60t vacuum degassing refining furnace and 4 sets of 1-20t electroslag re-melting furnaces.