GB 3Cr2Mo | DIN 1.2311 | ASTM P20 Plastic Mould Steel
AISI P20 Steel Plate Material is a versatile, low-alloy tool steel that is characterized by good toughness at moderate strength levels. The special purpose mold steel P20 steel plate is commonly used for plastic injection mold cavities and tooling and for die casting dies for zinc. P20 mold steel plate material is typically sold in the pre-hardened condition at a hardness of approximately 300 HBW.
2: P20 Steel equivalent
| Country | USA | German | GB/T |
| Standard | ASTM A681 | DIN EN ISO 4957 | GB/T 1299 |
| Grade | P20 | 1.2311 | 3Cr2Mo |
| Grade | C | Si | Mn | P | S | Cr | Mo |
| P20 | 0.28-0.4 | 0.2-0.8 | 0.6-1 | 0.03 | 0.03 | 1.4-2 | 0.3-0.55 |
| 1.2311 | 0.35-0.45 | 0.2-0.4 | 1.3-1.6 | 0.03 | 0.03 | 1.8-2.1 | 0.15-0.25 |
| 3Cr2Mo | 0.28-0.4 | 0.2-0.8 | 0.6-1 | 0.03 | 0.03 | 1.4-2 | 0.3-0.55 |
The mechanical properties mainly include tensile strength, yield strength, elongation, area or reduction, hardness, impact value, non-metalic inclusion etc. Different heat treatment, the mechanical properties will be different, such as normalized, tempered, QT. If you want to know the properties, kindly contact the salesman.
5: P20 steel overviews
| Size | Round | Dia 200-1000mm |
| Plate/Flat/Block | Thickness 16mm-100mm |
|
| Width 200mm-2000mm |
||
| Heat treatment | Normalized ; Annealed ; Quenched ; Tempered | |
| Surface condition | Black; Peeled; Polished; Machined; Grinded; Turned; Milled | |
| Delivery condition | Forged; Hot rolled; Cold drawn | |
| Test | Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc. | |
| Payment terms | T/T;L/C;/Money gram/ Paypal | |
| Trade terms | FOB; CIF; C&F; etc.. | |
| Delivery time | 30-45 days | |
| Application |
P20 tool steels are used for low temperature applications that include injection molds and die casting dies. Main applications of P20 steel plate and bar; Plastic moulds, die holder, backers, rames for plastic pressure dies, hydro forming mold tools.bolsters, die holders. Also suitable for other applications such as rails, shafts and wear strips. |
|
6. Heat Treatment
Stress Relieving
Preheating: Because mold steel P20 steel plate is sold in a pre-hardened condition, hardening heat treatment is not necessary. After machining and intermittently during service, the steel must be thermally stress relieved by heating to 900oF (482oC), equalizing and holding for one hour per inch (25.4mm) of thickness, and cooling in air to ambient temperature.
In those rare circumstances where the AISI steel P20 must be re-hardened, the steel must first be annealed prior to hardening.
Hardening
Critical Temperature: Ac1: 1405oF (763oC)
Preheating of P20 metal: Heat at a rate not exceeding 400oF per hour (222oC per hour) to 1150-1250oF (621-677oC) and equalize.
Austenitizing (High Heat)
Heat rapidly from the preheat to 1550oF (843°C). Soak for 30 minutes for first inch (25.4mm) of thickness, plus 15 minutes for each additional inch (25.4mm).
Quenching
Pressurized gas, or interrupted oil to 150-125oF (66-51oC).
For oil, quench until black, at about 900°F (482°C), then cool in still air to 150-125°F (66-51°C).
Tempering
P20 tool steels are tempered at 482-593°C (900 to 1100°F) for a Rockwell C hardness of 37 to 28.
Annealing
Annealing for AISI P20 tool steels takes place at 760-788°C (1400 to 1450°F) and then the steels are cooled slowly in the furnace at a temperature less than 4°C (40°F) per hour.
6: Delivery condition
For hot rolled plate, usually the delivery condition is hot rolled, annealed/QT, black surface;
| GB GB/T 1299 |
JIS JIS G4404 |
DIN (W-Nr.) DIN EN ISO4957 |
AISI/ASTM ASTM A681 |
BS BS 4659 |
| Cold Work Tool Steel | ||||
| Cr12 | SKD1 | 1.2080/X210Cr12 | D3 | |
| Cr5Mo1V | SKD12 | 1.2363/X100CrMoV5 | A2/T30102 | BA2 |
| Cr12MoV | 1.2601 | D5 | ||
| Cr12Mo1V1 | SKD11 | 1.2379/X153CrMo12 | D2 | |
| X210CrW12 | SKD2 | 1.2436 | D6 | |
| 9CrWMn | SKS3 | 1.2510/100MnCrW4 | O1 | |
| 9Mn2V | 1.2842 / 90MnCrV8 | O2 | B02 | |
| 5CrNiMo | SKT4 | 1.2713 | L6/T61206 | BH224/5 |
| Hot work Tool Steel | ||||
| 1.2355/50CrMoV13-15 | S7/T41907 | |||
| 5CrNiMoV | 1.2714 | 6F3 | ||
| 5CrNi4Mo | 1.2767 | 6F7 | ||
| SKD7 | 1.2365/32CrMoV12-28 | H10/T20810 | BH10 | |
| 4Cr5MoV | SKD6 | 1.2343/X37CrMoV5-1 | H11/T20811 | BH11 |
| 4Cr5MoSiV1 | SKD61 | 1.2344/X40CrMoV5-1 | H13 | |
| SKD62 | 1.2605/X35CrWMoV5 | H12/T20812 | BH12 | |
| 3Cr2W8V | SKD5 | 1.2581 | H21 | |
| Plastic Mould Steel | ||||
| 3Cr2Mo | 1.2311 | P20 | ||
| NAK80 | 1.2312 | P20+S / P21 | ||
| 3Cr2MnNiMo | 1.2738 | P20+Ni / 718 | ||
| 4Cr13 | SUS420J2 | 1.2083 | 415 | |
| 3Cr17+S | SUS420F | 1.2085 | ||
| 3Cr17Mo | SUS420J | 1.2316 | ||
| Engineering Steel | ||||
| GB GB/T 699 |
JIS JIS G4051 |
DIN (W-Nr.) EN 10083-2 |
AISI/ASTM ASTM A20 |
EN / BS |
| 1018 | EN2C | |||
| 20 | S20C | C20/1.1151 | 1020 | EN3B /070M20 |
| S35C | C35 | 1035 | ||
| 1040 | EN8/080M40 | |||
| 45 | S45C | C45/1.1191 | 1045 | EN8D/C45E |
| 50 | S50C | 1050 | ||
| S55C | 1055 | EN9/070M55 | ||
| Q345 | S355/ST52-3/1.1170 | EN14/150M19 | ||
| GB GB/T 3077 |
JIS JIS G4105/JIS G4103 |
DIN (W-Nr.) EN 10250 |
AISI/ASTM ASTM A29 |
BS BS 970 |
| 40Cr | SCr440 | 41Cr4(1.7035) | 5140 | |
| SCM420 | 18CrMo4/1.7243 | 4118 | ||
| 30CrMo | SCM430 | 25CrMo4/1.7218 | 4130 | 708A25/708M25 |
| 42CrMo | SCM440 | 42crmo4/1.7225 | 4140 | EN19/709M40 |
| 4145 | ||||
| 4330 | ||||
| 40CrNiMoA | SNCM 439/SNCM8 | 36CrNiMo4/1.6511 | 4340 | EN24/817M40 |
| 40NiMoCr10-5/1.6745 | EN26 | |||
| 34CrNiMo6 / 1.6582 | 4337 | |||
| 30CrNiMo16-6/1.6747 | EN30B/835M30 | |||
| 32CrMo12/1.7361 | EN40B/722M24 | |||
| SCM415 | 16MnCr5 / 1.7131 | 5115 | ||
| 15CrNi6/1.5919 | 3115 | |||
| 16NiCr4/1.5714 | EN351/635M15 | |||
| 4615/4617 | EN34/665M17 | |||
| 14NiCr4/1.5752 | 3310/3415 | EN36/655M13 | ||
| 15NiCrMo16-5/1.6723 | EN39/835M15 | |||
| 18CrNiMo7-6 (1.6587) | 4815 | |||
| SNCM220 | 1.6523/21NiCrMo2 | 8620 | 805M20 | |
| 20CrNiMo5 | EN353 | |||
| GCr15 | 52100/1.3505 | EN31/535A99 | ||
| Stainless Steel | ||||
| SUS440C | X105CrMo17/1.4125 | S44004/440C | ||
| Wear-resisting Steel | ||||
| GB | JIS | DIN (W-Nr.) | AISI/ASTM | SSAB |
| NM400 | HB400 | |||
| NM500 | HB500 | |||
| Spring Steel | ||||
| GB | JIS | DIN (W-Nr.) | AISI/ASTM | SSAB |
| 65MN | 1066 | |||
| 60Si2Mn | SUP6 | 60Si7 | 9260 | |
| 60Si2MnA | SUP7 | 60Si7 | 9260 | |
| 55CrMnA | SUP9 | 55Cr3 | 5155 | |
| 60CrMnA | SUP9A | 5160 | ||
| 50CrVA | SUP10 | 51CrV4 | 6150 | |
| High Speed Steel | ||||
| GB | JIS JIS G4403 |
DIN (W-Nr.) DIN EN ISO 4957 |
AISI/ASTM ASTM A600 |
BS BS 4659 |
| SKH51 | 1.3343 | M2 | ||
| SKH55 | 1.3243/HS6-5-2-5 | M35 | ||
| SKH59 | 1.3247/HS2-9-1-8 | M42 | ||
| SKH2 | HS18-0-1/1.3355 | T1 | ||
| SKH3 | S 18-1-2-5/1.3255 | T4/T12004 | ||
| SKH4 | 1.3265/S18-1-2-10 | T5/T12005 | BT5 | |
| All kinds of forging parts according to Drawing | ||||
| Size | Round | Dia 8-1200mm |
| Plate/Flat/Block | Thickness 10mm-800mm |
|
| Width 20mm-2000mm |
||
| Heat treatment | Normalized ; Annealed ; Quenched ; Tempered | |
| Surface condition | Black; Peeled; Polished; Machined; Grinded; Turned; Milled | |
| Delivery condition | Forged; Hot rolled; Cold drawn | |
| Test | Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc. | |
| Payment terms | T/T;L/C;/Money gram/ Paypal | |
| Trade terms | FOB; CIF; C&F; etc.. | |
| Delivery time | 30-45 days | |
Hunan Qilu Industrial Co., Ltd has the capacity to forge round steel, steel flat, square steel, module, shaft and roller, etc. The main specifications of the products include Φ80-1000mm forging materials and 80-1200mm square billets and which the maximum piece weight can reach 50T.
The company owns advanced special steel smelting facilities and forging processing equipments, the main steel-making equipment include 2 sets of 50t ultra-high power electric arc furnaces,2 sets of 60t LF refining furnaces,1 set of 60t vacuum degassing refining furnace and 4 sets of 1-20t electroslag re-melting furnaces.