GB 45 | JIS S45C | DIN C45/1.1191 | BS EN8D/C45E | ASTM 1045 Engineering Steel
1: C45 steel introduction
C45 is a kind of medium carbon high quality steel with high strength. Due to poor hardenability, it is generally used in normalizing state. When the mechanical property is required to be high, quenching and tempering treatment is adopted. Cold deformation plasticity is medium, annealing and normalizing machinability is better than quenching and tempering.
2: C45 steel equivalent
| Country | China | Japan | Germany | USA |
| Standard | GB/T | JIS |
DIN (W-Nr.) DIN 17200 |
AISI/ASTM |
| Grade | C45 |
3: C45 steel chemical composition
| Grade | C | Si | Mn | P | S |
| C45 | 0.42-0.50 | 0.40 | 0.50-0.80 | 0.045 | 0.045 |
4: C45 steel mechanical properties
The mechanical properties mainly include tensile strength, yield strength, elongation, area or reduction, hardness, impact value, non-metalic inclusion etc. Different heat treatment, the mechanical properties will be different, such as normalized, tempered, QT. If you want to know the properties, kindly contact the salesman.
5: C45 steel overviews
| Size | Round | Dia 6-1200mm |
| Plate/Flat/Block | Thickness 6mm-500mm |
|
| Width 20mm-1000mm |
||
| Heat treatment | Normalized ; Annealed ; Quenched ; Tempered | |
| Surface condition | Black; Peeled; Polished; Machined; Grinded; Turned; Milled | |
| Delivery condition | Forged; Hot rolled; Cold drawn | |
| Test | Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc. | |
| Payment terms | T/T;L/C;/Money gram/ Paypal | |
| Trade terms | FOB; CIF; C&F; etc.. | |
| Delivery time | 30-45 days | |
| Application | C45 is used to manufacture parts with high strength requirements, such as gears, shafts, piston pins, etc., and machined parts, forgings, stamping parts, bolts, nuts and pipe joints with low stress. | |
6: Delivery condition
For hot forged bar, usually the delivery condition is hot forged, annealed/QT, rough turned/Black surface.
For hot rolled bar, usually the delivery condition is hot rolled, annealed/QT, Black surface.
For hot forged block, usually the delivery condition is hot forged, annealed/QT, milled surface/Black surface
For hot rolled plate, usually the delivery condition is hot rolled, annealed/QT, black surface.
For cold drawn bar, usually the delivery condition is cold drawn, annealed/QT, peeled/black surface
| GB GB/T 1299 |
JIS JIS G4404 |
DIN (W-Nr.) DIN EN ISO4957 |
AISI/ASTM ASTM A681 |
BS BS 4659 |
| Cold Work Tool Steel | ||||
| Cr12 | SKD1 | 1.2080/X210Cr12 | D3 | |
| Cr5Mo1V | SKD12 | 1.2363/X100CrMoV5 | A2/T30102 | BA2 |
| Cr12MoV | 1.2601 | D5 | ||
| Cr12Mo1V1 | SKD11 | 1.2379/X153CrMo12 | D2 | |
| X210CrW12 | SKD2 | 1.2436 | D6 | |
| 9CrWMn | SKS3 | 1.2510/100MnCrW4 | O1 | |
| 9Mn2V | 1.2842 / 90MnCrV8 | O2 | B02 | |
| 5CrNiMo | SKT4 | 1.2713 | L6/T61206 | BH224/5 |
| Hot work Tool Steel | ||||
| 1.2355/50CrMoV13-15 | S7/T41907 | |||
| 5CrNiMoV | 1.2714 | 6F3 | ||
| 5CrNi4Mo | 1.2767 | 6F7 | ||
| SKD7 | 1.2365/32CrMoV12-28 | H10/T20810 | BH10 | |
| 4Cr5MoV | SKD6 | 1.2343/X37CrMoV5-1 | H11/T20811 | BH11 |
| 4Cr5MoSiV1 | SKD61 | 1.2344/X40CrMoV5-1 | H13 | |
| SKD62 | 1.2605/X35CrWMoV5 | H12/T20812 | BH12 | |
| 3Cr2W8V | SKD5 | 1.2581 | H21 | |
| Plastic Mould Steel | ||||
| 3Cr2Mo | 1.2311 | P20 | ||
| NAK80 | 1.2312 | P20+S / P21 | ||
| 3Cr2MnNiMo | 1.2738 | P20+Ni / 718 | ||
| 4Cr13 | SUS420J2 | 1.2083 | 415 | |
| 3Cr17+S | SUS420F | 1.2085 | ||
| 3Cr17Mo | SUS420J | 1.2316 | ||
| Engineering Steel | ||||
| GB GB/T 699 |
JIS JIS G4051 |
DIN (W-Nr.) EN 10083-2 |
AISI/ASTM ASTM A20 |
EN / BS |
| 1018 | EN2C | |||
| 20 | S20C | C20/1.1151 | 1020 | EN3B /070M20 |
| S35C | C35 | 1035 | ||
| 1040 | EN8/080M40 | |||
| 45 | S45C | C45/1.1191 | 1045 | EN8D/C45E |
| 50 | S50C | 1050 | ||
| S55C | 1055 | EN9/070M55 | ||
| Q345 | S355/ST52-3/1.1170 | EN14/150M19 | ||
| GB GB/T 3077 |
JIS JIS G4105/JIS G4103 |
DIN (W-Nr.) EN 10250 |
AISI/ASTM ASTM A29 |
BS BS 970 |
| 40Cr | SCr440 | 41Cr4(1.7035) | 5140 | |
| SCM420 | 18CrMo4/1.7243 | 4118 | ||
| 30CrMo | SCM430 | 25CrMo4/1.7218 | 4130 | 708A25/708M25 |
| 42CrMo | SCM440 | 42crmo4/1.7225 | 4140 | EN19/709M40 |
| 4145 | ||||
| 4330 | ||||
| 40CrNiMoA | SNCM 439/SNCM8 | 36CrNiMo4/1.6511 | 4340 | EN24/817M40 |
| 40NiMoCr10-5/1.6745 | EN26 | |||
| 34CrNiMo6 / 1.6582 | 4337 | |||
| 30CrNiMo16-6/1.6747 | EN30B/835M30 | |||
| 32CrMo12/1.7361 | EN40B/722M24 | |||
| SCM415 | 16MnCr5 / 1.7131 | 5115 | ||
| 15CrNi6/1.5919 | 3115 | |||
| 16NiCr4/1.5714 | EN351/635M15 | |||
| 4615/4617 | EN34/665M17 | |||
| 14NiCr4/1.5752 | 3310/3415 | EN36/655M13 | ||
| 15NiCrMo16-5/1.6723 | EN39/835M15 | |||
| 18CrNiMo7-6 (1.6587) | 4815 | |||
| SNCM220 | 1.6523/21NiCrMo2 | 8620 | 805M20 | |
| 20CrNiMo5 | EN353 | |||
| GCr15 | 52100/1.3505 | EN31/535A99 | ||
| Stainless Steel | ||||
| SUS440C | X105CrMo17/1.4125 | S44004/440C | ||
| Wear-resisting Steel | ||||
| GB | JIS | DIN (W-Nr.) | AISI/ASTM | SSAB |
| NM400 | HB400 | |||
| NM500 | HB500 | |||
| Spring Steel | ||||
| GB | JIS | DIN (W-Nr.) | AISI/ASTM | SSAB |
| 65MN | 1066 | |||
| 60Si2Mn | SUP6 | 60Si7 | 9260 | |
| 60Si2MnA | SUP7 | 60Si7 | 9260 | |
| 55CrMnA | SUP9 | 55Cr3 | 5155 | |
| 60CrMnA | SUP9A | 5160 | ||
| 50CrVA | SUP10 | 51CrV4 | 6150 | |
| High Speed Steel | ||||
| GB | JIS JIS G4403 |
DIN (W-Nr.) DIN EN ISO 4957 |
AISI/ASTM ASTM A600 |
BS BS 4659 |
| SKH51 | 1.3343 | M2 | ||
| SKH55 | 1.3243/HS6-5-2-5 | M35 | ||
| SKH59 | 1.3247/HS2-9-1-8 | M42 | ||
| SKH2 | HS18-0-1/1.3355 | T1 | ||
| SKH3 | S 18-1-2-5/1.3255 | T4/T12004 | ||
| SKH4 | 1.3265/S18-1-2-10 | T5/T12005 | BT5 | |
| All kinds of forging parts according to Drawing | ||||
| Size | Round | Dia 8-1200mm |
| Plate/Flat/Block | Thickness 10mm-800mm |
|
| Width 20mm-2000mm |
||
| Heat treatment | Normalized ; Annealed ; Quenched ; Tempered | |
| Surface condition | Black; Peeled; Polished; Machined; Grinded; Turned; Milled | |
| Delivery condition | Forged; Hot rolled; Cold drawn | |
| Test | Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc. | |
| Payment terms | T/T;L/C;/Money gram/ Paypal | |
| Trade terms | FOB; CIF; C&F; etc.. | |
| Delivery time | 30-45 days | |
Hunan Qilu Industrial Co., Ltd has the capacity to forge round steel, steel flat, square steel, module, shaft and roller, etc. The main specifications of the products include Φ80-1000mm forging materials and 80-1200mm square billets and which the maximum piece weight can reach 50T.
The company owns advanced special steel smelting facilities and forging processing equipments, the main steel-making equipment include 2 sets of 50t ultra-high power electric arc furnaces,2 sets of 60t LF refining furnaces,1 set of 60t vacuum degassing refining furnace and 4 sets of 1-20t electroslag re-melting furnaces.